| Peer-Reviewed

Comparative Evaluation of the Photodegradation of Stearic Acid by TiO2 - Modified Cement Under UV Irradiation Through Water Contact Angle and Absorbance Studies

Received: 22 November 2019     Accepted: 17 December 2019     Published: 23 March 2020
Views:       Downloads:
Abstract

The photodegradation of stearic acid has been studied through evaluation of changes in the contact angles of water and from absorbance measurements. The photodegradation of 0.02 M stearic acid coatings and solutions were initiated by TiO2 nanoparticles of average size of 9.80 ± 2.92 nm embedded in cements in 1.66 wt.%, 3.33 wt.%, 5.0 wt.% and 6.67 wt.% to generate modified cement composites with photocatalytic capability. It was noted that the photodegradation efficiencies increased with the increase in the weight-percent of TiO2 present in the modified cement samples. A modified Cassie-Baxter and the Langmuir-Hinselwood models were used to compute the rate constants, based on changes in the contact angles of water and in the concentration of the stearic acid respectively, on exposure to the UV light source. The modified Cassie-Baxter model successfully provided a route to relate the changes in water contact angle to the rate of photodegradation of a hydrophobic, long-chain stearic acid. The values of the rate constant estimated from both models increased with increase in the amount of TiO2 present in the modified cement samples. However, the rate constant values obtained from the modified Cassie-Baxter model were lower than those obtained from the Langmuir-Hinselwood model. The values of these rate contants were in the range of 0.11-0.50 hr-1 and 0.78-1.33 hr-1 as btained from the modified Cassie-Baxter and Langmuir-Hinselwood models respectively. This disparity in the values was attributed to a higher mobility of the charge carriers and free-radicals that induced the photodegradation in liquid medium as compared to the solid medium.

Published in Advances in Materials (Volume 9, Issue 1)
DOI 10.11648/j.am.20200901.11
Page(s) 1-7
Creative Commons

This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.

Copyright

Copyright © The Author(s), 2020. Published by Science Publishing Group

Keywords

Photodegradation, UV Irradiation, Stearic Acid, Contact Angle, Absorbance

References
[1] K. M. Lee, S. B. Abd Hamid, C. W. Lai, J. Nanomater. 2015, 1, (2015).
[2] C. Tizaoui, K. Mezughi, R. Bickley, Desalination, 273, 197, (2011).
[3] I. Kim, H. Tanaka, Environ. Int., 35 (5), 793, (2009).
[4] E. Yousif, R. Haddad, SpringerPlus, 2, 398, (2013).
[5] M. R. Hoffman, S. T. Martin, W. Choi, D. W. Bahnemann, Chem. Rev., 95, 69, (1995).
[6] N. Smirnova, T. Fesenko, M. Zhukovsky, J. Goworek, A. Eremenko, Nanoscale Res. Lett., 10 (1), 500, (2015).
[7] T. Zubkov, D. Stahl, T. L. Thompson, D. Panayotov, O. Diwald, J. T. Yates, J. Phy. Chem. B, 109 (32), 15454, (2005).
[8] J. M. White, J. Szanyi, M. A. Henderson, J. Phy. Chem. B, 107 (34), 9029, (2003).
[9] P. S. Foran, C. Boxall, K. R. Denison, Langmuir, 28 (51), 17647, (2012).
[10] J. Kumar, A. Srivastava, A. Bansal, Int. J. Innov. Res. Sci. Eng. Technol., 2 (7), 2688, (2013).
[11] R. Khataee, V. Heydari, L. Moradkhannejhad, M. Safarpour, S. W. Joo, J. Nanosci. Nanotech., 13, 5109–5114, (2013).
[12] A. M. Ramirez, K. Demeestere, N. De Belie, T. Mäntylä, E. Levänen, Build. Environ., 45 (4), 832, (2010).
[13] A. Hadj Aïssa, E. Puzenat, A. Plassais, J M. Herrmann, C. Haehnel, C. Guillard, Appl. Cataly B-Env, 107 (1-2), 1, (2011).
[14] A. Strini, L. Schiavi, Appl. Cataly. B-Env., 103 (1-2), 226, (2011).
[15] L. Cassar, A. Beeldens, N. Pimpinelli, and G. L. Guerrini, ‘‘Photocatalysis of Cementitious Materials’’; International RILEM Symposium onPhotocatalysis, Environment and Construction Materials, Vol. 1, pp. 131-145, 2007.
[16] M. Janus, K. Bubac, J. Zatorska, E. Kusiak-Nejman, A. Czyżewski, A. W. Morawski. Pol. J. Chem. Technol., 17, 96, (2015).
[17] I. Karatasis, M. S. Katsiotis, V. Likodimos, A. Kontos, G. Papavassiliou, P. Falaras, V. Kilikoglou. Appl. Cataly. B-Env. 95 (1-2), 78, (2009).
[18] M. Lackhoff, X. Prieto, N. Nestle, F. Dehn, R. Niessner. Appl. Cataly. B-Env., 43 (3), 205, (2003).
[19] A. Yousouffi, A. Allahverdi, P. Hejazi, Constr. Build Mater., 41, 224, (2013).
[20] T. Meng, Y. Yu, X. Qian, S. Zhan, K. Qian, Constr Build Mater. 29, 241, (2012).
[21] Peter Atkins, Physical Chemistry, 6th Ed, 1998, pg 458.
[22] J. Vicente, T. Gacoin, P. Barboux, J. Boilot, M. Rondet, L. Gueneau, International Journal of Photoenergy, 5, 1, (2003).
[23] A. Fujishima, T. Rao, D. Tryk, J Photochem Photobiol C. Photochem Rev 1, 1,(2000).
[24] M. Cho, H. Chung, W. Choi, J. Yoon, Water Res., 38 (4), 1069, (2004).
[25] M. Fathinia, A. R. Khataee, M. Zarei, and S. Aber, J. Mol. Catal. A: Chem., 333 (1-2), 73, (2010).
[26] A. Fujishima, K. Honda. Nature, 238 (5358), 3, (1972).
[27] R. Wang, K. Hashimoto, A. Fujishima, M. Chikuni, E, Kojima, A. Kitamura. Nature, 388, 431, (1997).
[28] K. Seki, M. Tachiya, J. Phys. Chem. B, 108 (15), 4806, (2004).
[29] B. Ruot, A. Plassais, F. Olive, L. Guillot, L., Sol Energy, 83 (10), 1794, (2009).
[30] K. Hayat, M. A. Gondal, M. M. Khaled, S. Ahmed, and A. M. Shemsi. Appl Catal A- Gen., 393 (1-2), 122, (2011).
[31] B. Gao, P. S. Yap, T. M Lim, T. T. Lim. Chem. Eng. J., 171 (3), 1098, (2011).
[32] E. Quagliarini, F. Bondioli, G. B. Goffredo, C. Cordoni, P. Munafò, Constr. Build. Mater., 37, 51, (2012).
[33] A. Mills, S. Le Hunte, J. Photochem. Photobio., 108 (1), 1, (1997).
[34] A. V. Emeline, V. Ryabchuk, N. Serpone, J. Photochem. Photobio. A, 133 (1-2), 89, (2000).
[35] A. Mills, J. Wang, D. F. Ollis, J Catal., 243 (1), 1, (2006)
[36] A. B. D. Cassie, S. Baxter, T. Faraday Soc., 40, 546, (1944).
Cite This Article
  • APA Style

    Aniedi Nyong, Edet Nsi, Joachim Awaka-Ama, Godwin Udo. (2020). Comparative Evaluation of the Photodegradation of Stearic Acid by TiO2 - Modified Cement Under UV Irradiation Through Water Contact Angle and Absorbance Studies. Advances in Materials, 9(1), 1-7. https://doi.org/10.11648/j.am.20200901.11

    Copy | Download

    ACS Style

    Aniedi Nyong; Edet Nsi; Joachim Awaka-Ama; Godwin Udo. Comparative Evaluation of the Photodegradation of Stearic Acid by TiO2 - Modified Cement Under UV Irradiation Through Water Contact Angle and Absorbance Studies. Adv. Mater. 2020, 9(1), 1-7. doi: 10.11648/j.am.20200901.11

    Copy | Download

    AMA Style

    Aniedi Nyong, Edet Nsi, Joachim Awaka-Ama, Godwin Udo. Comparative Evaluation of the Photodegradation of Stearic Acid by TiO2 - Modified Cement Under UV Irradiation Through Water Contact Angle and Absorbance Studies. Adv Mater. 2020;9(1):1-7. doi: 10.11648/j.am.20200901.11

    Copy | Download

  • @article{10.11648/j.am.20200901.11,
      author = {Aniedi Nyong and Edet Nsi and Joachim Awaka-Ama and Godwin Udo},
      title = {Comparative Evaluation of the Photodegradation of Stearic Acid by TiO2 - Modified Cement Under UV Irradiation Through Water Contact Angle and Absorbance Studies},
      journal = {Advances in Materials},
      volume = {9},
      number = {1},
      pages = {1-7},
      doi = {10.11648/j.am.20200901.11},
      url = {https://doi.org/10.11648/j.am.20200901.11},
      eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.am.20200901.11},
      abstract = {The photodegradation of stearic acid has been studied through evaluation of changes in the contact angles of water and from absorbance measurements. The photodegradation of 0.02 M stearic acid coatings and solutions were initiated by TiO2 nanoparticles of average size of 9.80 ± 2.92 nm embedded in cements in 1.66 wt.%, 3.33 wt.%, 5.0 wt.% and 6.67 wt.% to generate modified cement composites with photocatalytic capability. It was noted that the photodegradation efficiencies increased with the increase in the weight-percent of TiO2 present in the modified cement samples. A modified Cassie-Baxter and the Langmuir-Hinselwood models were used to compute the rate constants, based on changes in the contact angles of water and in the concentration of the stearic acid respectively, on exposure to the UV light source. The modified Cassie-Baxter model successfully provided a route to relate the changes in water contact angle to the rate of photodegradation of a hydrophobic, long-chain stearic acid. The values of the rate constant estimated from both models increased with increase in the amount of TiO2 present in the modified cement samples. However, the rate constant values obtained from the modified Cassie-Baxter model were lower than those obtained from the Langmuir-Hinselwood model. The values of these rate contants were in the range of 0.11-0.50 hr-1 and 0.78-1.33 hr-1 as btained from the modified Cassie-Baxter and Langmuir-Hinselwood models respectively. This disparity in the values was attributed to a higher mobility of the charge carriers and free-radicals that induced the photodegradation in liquid medium as compared to the solid medium.},
     year = {2020}
    }
    

    Copy | Download

  • TY  - JOUR
    T1  - Comparative Evaluation of the Photodegradation of Stearic Acid by TiO2 - Modified Cement Under UV Irradiation Through Water Contact Angle and Absorbance Studies
    AU  - Aniedi Nyong
    AU  - Edet Nsi
    AU  - Joachim Awaka-Ama
    AU  - Godwin Udo
    Y1  - 2020/03/23
    PY  - 2020
    N1  - https://doi.org/10.11648/j.am.20200901.11
    DO  - 10.11648/j.am.20200901.11
    T2  - Advances in Materials
    JF  - Advances in Materials
    JO  - Advances in Materials
    SP  - 1
    EP  - 7
    PB  - Science Publishing Group
    SN  - 2327-252X
    UR  - https://doi.org/10.11648/j.am.20200901.11
    AB  - The photodegradation of stearic acid has been studied through evaluation of changes in the contact angles of water and from absorbance measurements. The photodegradation of 0.02 M stearic acid coatings and solutions were initiated by TiO2 nanoparticles of average size of 9.80 ± 2.92 nm embedded in cements in 1.66 wt.%, 3.33 wt.%, 5.0 wt.% and 6.67 wt.% to generate modified cement composites with photocatalytic capability. It was noted that the photodegradation efficiencies increased with the increase in the weight-percent of TiO2 present in the modified cement samples. A modified Cassie-Baxter and the Langmuir-Hinselwood models were used to compute the rate constants, based on changes in the contact angles of water and in the concentration of the stearic acid respectively, on exposure to the UV light source. The modified Cassie-Baxter model successfully provided a route to relate the changes in water contact angle to the rate of photodegradation of a hydrophobic, long-chain stearic acid. The values of the rate constant estimated from both models increased with increase in the amount of TiO2 present in the modified cement samples. However, the rate constant values obtained from the modified Cassie-Baxter model were lower than those obtained from the Langmuir-Hinselwood model. The values of these rate contants were in the range of 0.11-0.50 hr-1 and 0.78-1.33 hr-1 as btained from the modified Cassie-Baxter and Langmuir-Hinselwood models respectively. This disparity in the values was attributed to a higher mobility of the charge carriers and free-radicals that induced the photodegradation in liquid medium as compared to the solid medium.
    VL  - 9
    IS  - 1
    ER  - 

    Copy | Download

Author Information
  • Materials Chemistry Research Unit, Department of Chemistry, Faculty of Physical Sciences, Akwa Ibom State University, Akwa Ibom State, Nigeria

  • Materials Chemistry Research Unit, Department of Chemistry, Faculty of Physical Sciences, Akwa Ibom State University, Akwa Ibom State, Nigeria

  • Materials Chemistry Research Unit, Department of Chemistry, Faculty of Physical Sciences, Akwa Ibom State University, Akwa Ibom State, Nigeria

  • Materials Chemistry Research Unit, Department of Chemistry, Faculty of Physical Sciences, Akwa Ibom State University, Akwa Ibom State, Nigeria

  • Sections